“e-mateX®FB-0530” is antistatic material composed of high-grade polycarbonate and carbon fiber. The material can be used for parts which require abrasion resistance and high stiffness. Also, it has excellent properties of low outgassing, stiffness and prevents static charge.
In-process storage case/box and in-process jigs
| Physical Properties | Composition |
|---|---|
| e-mateX® FB-0530 antistatic black in color | |
| Surface Resistance (Ω/□): ASTM D-257 | 104–105 |
| Density (g/cm³): ASTM D-792 | 1.23 |
| Yield Stress in Tension (Mpa): ASTM D-638 | 108 |
| Tensile Strain at Break (%): ASTM D-638 | 4 |
| Flexural Strength (Mpa): ASTM D-790 | 167 |
| Flexural Modulus (Mpa): ASTM D-790 | 6080 |
| Isot Impact Strength (J/m): ASTM D-256 (t=6.4mm) | 78 |
| Deflection Temperature under Load (℃): ASTM D-648 (6.4mm×0.45Mpa), ASTM D-648 (6.4mm×1.82Mpa) |
142（6.4mm×1.82Mpa) |
| Rockwell Hardness: ASTM D-785 (R scale, Load Weight 60) | 123 |
Note: The values stated here are representative values, not standard ones.